Processing of titanium and titanium alloy forging heating temperature (physical properties)
Numbering
(α+β)/β phase transition point / °C
Ingot
Deformed blank
Finished product
Heating temperature / °C
Final forging temperature / ≮ °C
Heating temperature / °C
Final forging temperature / °C
Heating temperature / °C
Final forging temperature / ≮ °C
TA1
890-920
1000-1020
750
900-950
700
850-880
700
TA2
890-920
1000-1020
750
900-950
700
850-880
700
TA3
890-920
1000-1020
750
900-950
700
850-880
700
TA4
960-980
1150
850
1030-1050
800
-
-
TA5
980-1000
1080-1150
850
1000-1050
800
-
-
TA6
1000-1020
1150-1200
900
1050-1100
850
980-1020
800
TA7
1000-1020
1150-1200
900
1050-1100
850
980-1020
800
TB2
750
1140-1160
850
1090-1100
800
990-1010
800
TC1
910-930
1000-1020
750
900-950
750
850-880
750
TC2
920-940
1000-1020
800
900-950
800
850-900
750
TC3
960-970
1100-1150
850
950-1050
800
950-970
750
TC4
980-990
1100-1150
850
960-1100
800
950-970
750
TC6
950-980
1150-1180
850
1000-1050
800
950-980
800
TC9
1000-1020
1140-1160
850
1050-1080
800
950-970
800
TC10
935
1100-1150
800
1000-1050
800
930-940
800

Copper Briquette Machine

There are many problems in the recovery of copper chips directly into the furnace, the recycling of copper brass chips reduces the production cost of foundry enterprises and greatly improves the market competitiveness of the enterprises. The copper scraps are small, loose, directly into the furnace will be seriously blocked, the material block clearance is the furnace gas rising channel, directly affect the smelting process, the loose steel scrap without pressing, extremely easy to float on the furnace lining, corrosion lining, and large loss of raw materials will cause low molten iron rate.

Copper Briquetter, Brass Briquette Machine, Copper Chips Briquette Machine, Copper Briquetting Press, Copper Briquetting Machine

Jiangyin Metallurgy Hydraulic Machinery Factory , https://www.jiangyinyejing.com